Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
Forum rules
If you need help logging in, or have question about how something works, use the Support forum located here Support Forum
Complete set of Forum Rules Forum Rules
If you need help logging in, or have question about how something works, use the Support forum located here Support Forum
Complete set of Forum Rules Forum Rules
-
Topic author - Posts: 152
- Joined: Tue Jan 15, 2019 11:30 am
- First Name: James
- Last Name: Lyons
- * REQUIRED* Type and Year of Model Ts owned: 1913 Touring, 1915 Touring, 1925 Coupe
- Location: West Virginia
- MTFCA Number: 10000
Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
I pulled the engine out of my 1925 Coupe. It had a few things wrong with it so I decided to take it out. First thing I did is have the crankshaft magnafluxed as always. In the attached photo, you will see a photograph of a 1/4 inch long crack in the #4 rod journal. I am considering putting it back in the car. Here are my reasons why. Please keep your rebuttals polite and thought-provoking. Making a blanket statement of "ITS CRACKED, REPLACE IT..." does nothing for good dialogue.
Here's why:
1, From the looks of the crack, and the fact that I can feel it with my fingernail tells me it's been there for years. The edge of the crack is rounded, speaking to years of use, polishing the sharp edge away to a rounded bevel.
2, The crack runs axially... along the length of the journal. If it ran diametrically, I would replace it without another thought. But this crack is not cutting the journal in two.
3, It's in the downward stroke side.... meaning it's in the crux of the crank, so when the piston fires, and pushes down hard on the journal, the crack is being forced closed... not open. I doubt this scenario promotes rapid crack growth.
In the end, I may choose to replace it. But a crack this small, running in this direction doesn't make my alarm bells go off. Forget that we live in a world of Scat cranks. If you only had this one to use, lets figure out what everyone thinks the probability of failure is?
And GO....
Here's why:
1, From the looks of the crack, and the fact that I can feel it with my fingernail tells me it's been there for years. The edge of the crack is rounded, speaking to years of use, polishing the sharp edge away to a rounded bevel.
2, The crack runs axially... along the length of the journal. If it ran diametrically, I would replace it without another thought. But this crack is not cutting the journal in two.
3, It's in the downward stroke side.... meaning it's in the crux of the crank, so when the piston fires, and pushes down hard on the journal, the crack is being forced closed... not open. I doubt this scenario promotes rapid crack growth.
In the end, I may choose to replace it. But a crack this small, running in this direction doesn't make my alarm bells go off. Forget that we live in a world of Scat cranks. If you only had this one to use, lets figure out what everyone thinks the probability of failure is?
And GO....
-
- Posts: 4967
- Joined: Sat Jan 05, 2019 1:57 pm
- First Name: Mark
- Last Name: Gregush
- * REQUIRED* Type and Year of Model Ts owned: 1925 cutdown PU, 1920 Dodge touring, 1948 F2 Ford flat head 6 pickup 3 speed
- Location: Portland Or
- MTFCA Number: 52564
- Board Member Since: 1999
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
Could just be a deep gouge. I would have it magnafluxed to check. On my own car if it passes that test I would use it, customers car no.
I know the voices aren't real but damn they have some good ideas!
1925 Cut down pickup
1920 Dodge touring
1948 Ford F2 pickup
1925 Cut down pickup
1920 Dodge touring
1948 Ford F2 pickup
-
- Posts: 97
- Joined: Wed Jan 09, 2019 6:46 pm
- First Name: John
- Last Name: Gulbankian
- Location: Massachusetts
- Contact:
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
You didn't say "Wet magnaflux" as if it was done dry it only gives a one dimensional image whereas the Wet mag will give all three.
-
- Posts: 4095
- Joined: Tue Jan 08, 2019 1:39 pm
- First Name: Norman
- Last Name: Kling
- Location: Alpine California
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
I think you are taking a big chance. If the car is rarely driven, then maybe you can get by for a while, however, it could break at any unexpected time and cause great damage to the engine or other parts. When it breaks, the car will suddenly stop and other parts could also break.
If you are planning to sell the car, it would also be unfair to the potential buyer if you were not to disclose this information. Also remember that this location has the most pressure of any place on the crankshaft because of the pressure of the first three cylinders firing, this location will not only take the pressure of number 4 but will be twisted by the other 3.
It is really a very lucky thing that you found this crack before anything broke because you might even be able to save the babbit. If your bearings are undersize, but the babbit is sound, you could bore them out to standard and fit a brand new crank in the engine. The new SKAT crank will cost a bit, but you can get one in standard stroke and the only difference is counterbalance. It really runs smooth and is stronger than the original crank.
So, the expenditure for a new crank now, could actually save you from having to replace the entire engine or even more in the future.
The decision is yours to make, but if it were mine, I would replace the crank.
Norm
If you are planning to sell the car, it would also be unfair to the potential buyer if you were not to disclose this information. Also remember that this location has the most pressure of any place on the crankshaft because of the pressure of the first three cylinders firing, this location will not only take the pressure of number 4 but will be twisted by the other 3.
It is really a very lucky thing that you found this crack before anything broke because you might even be able to save the babbit. If your bearings are undersize, but the babbit is sound, you could bore them out to standard and fit a brand new crank in the engine. The new SKAT crank will cost a bit, but you can get one in standard stroke and the only difference is counterbalance. It really runs smooth and is stronger than the original crank.
So, the expenditure for a new crank now, could actually save you from having to replace the entire engine or even more in the future.
The decision is yours to make, but if it were mine, I would replace the crank.
Norm
-
- Posts: 647
- Joined: Mon Jan 07, 2019 7:40 am
- First Name: CHARLIE
- Last Name: BRANCA
- * REQUIRED* Type and Year of Model Ts owned: "27 Tudor / "23 Touring
- Location: Brick N.J.
- MTFCA Number: 28967
- Board Member Since: 2010
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
Sounds a bit like you're trying to talk us and yourself into reusing it. At least do that follow up wet magnaflux test & make your decision based on that.
Forget everything you thought you knew.
-
Topic author - Posts: 152
- Joined: Tue Jan 15, 2019 11:30 am
- First Name: James
- Last Name: Lyons
- * REQUIRED* Type and Year of Model Ts owned: 1913 Touring, 1915 Touring, 1925 Coupe
- Location: West Virginia
- MTFCA Number: 10000
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
Charlie... you are not entirely wrong. I'm not trying to talk anyone else into anything. I'm just presenting what the shop found today, and my take on the crack. In response, I'm fishing for feedback. I never use this car. It hasn't had 100 miles put on it in the last 40 years.. But it's been in my family for 72 years and its here to stay. I at least want to be able to start it up and move it around.... maybe take it on a 10 mile run once a year. But it will NEVER be a tour car. And because of that, I cannot justify 1500 bucks for a Scat crank. So, I either need to find a good used crank that measures 1.245 all the way around, or calculate my probability of destruction...
-
- Posts: 404
- Joined: Sun Jan 06, 2019 5:39 pm
- First Name: Val
- Last Name: Soupios
- * REQUIRED* Type and Year of Model Ts owned: '10 touring, '12 touring, '13 hack, '14 runabout, '14 touring, '14 speedster, '22 centerdoor, '27 touring
- Location: Jupiter Florida
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
Why not have it x-rayed. I believe that is how they confirmed the quality of the weld on my 1908 Locomobile crank.
-
- Posts: 304
- Joined: Sun Mar 03, 2019 10:13 pm
- First Name: Dennis
- Last Name: Hoshield
- * REQUIRED* Type and Year of Model Ts owned: '24 RPU (Raodster converted to Pickup)
- Location: Petoskey, MI
- MTFCA Number: 24305
- Board Member Since: 2015
- Contact:
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
I don't have enough experience to say one way or another . I know I don't take the engine out of my car unless I have to! Lol...
My question is one of curiosity..... (Of course, now that I've started a reply, I don't remember if the crack was on a babbitt/bearing location, or attached to a rod.) In any case... What does it's mating surfaces look like? Is there a noticeable wear pattern where the crack is?
My question is one of curiosity..... (Of course, now that I've started a reply, I don't remember if the crack was on a babbitt/bearing location, or attached to a rod.) In any case... What does it's mating surfaces look like? Is there a noticeable wear pattern where the crack is?
'24 RPU
Petoskey, Mi
Petoskey, Mi
-
- Posts: 5339
- Joined: Sun Jan 06, 2019 11:09 am
- First Name: Henry
- Last Name: Lee
- * REQUIRED* Type and Year of Model Ts owned: Many
- Location: South Pittsburg, TN
- MTFCA Number: 479
- MTFCA Life Member: YES
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
James I believe the decision is yours and yours only. If you accept it and it does fail then you knew the risk. Either way having fun is what is all about.
On a side note.., knew a guy with the same issue some 40 years ago. As far as I know it is still running fine.
Hank
On a side note.., knew a guy with the same issue some 40 years ago. As far as I know it is still running fine.
Hank
-
- Posts: 1302
- Joined: Mon Jan 07, 2019 2:42 pm
- First Name: Frank
- Last Name: van Ekeren
- * REQUIRED* Type and Year of Model Ts owned: 1916 touring, 1916 pick-up, 1924 coupe, 1926 touring, 1927 touring
- Location: Rosedale Vic Australia
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
This has been debated a few times several years ago but I can't find it with a search, we all know that with a radial crack it's scrap, a time bomb waiting to go off but with a horizontal crack, no one has ever seen a crank split the length of a journal unless someone can say so now. The consensus back then was that many a shaft had horizontal cracks from maybe new and if not effecting the Babbitt any it wasn't to be an issue. But if it grows any more in length, what effect it will have on the bearing would be the big question. Choice is still going to be yours..
-
- Posts: 107
- Joined: Sat Feb 09, 2019 7:17 pm
- First Name: Frank
- Last Name: Iaccino
- Location: Hudson, NY
- MTFCA Number: 17726
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
I'm not sure where you are in W Virginia, but I'm going to be set up in Carlisle next week in spot D33-35 and I can bring two used crank shafts for you to look at. They both have been magnafluxed and polished on a crank machine (not ground, polished). The both have standard mains and .010 under rod journals. Either one, $200.
Frank
518-755-0986
Frank
518-755-0986
-
- Posts: 1055
- Joined: Sat Apr 13, 2019 6:06 pm
- First Name: Susanne
- Last Name: Rohner
- * REQUIRED* Type and Year of Model Ts owned: Late '15 touring, "Angel".
- Location: Valfabbrica, (central) Italy
- MTFCA Number: 464
- MTFCA Life Member: YES
- Board Member Since: 1999
- Contact:
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
Even if it's not a radial crack, it's evidence of crystalized metal structure in the crank. Even if it doesn't go now, nothing is saying that you won't develop a radial crack in that crystallized metal structure. How much is your time, patience, and engine worth? If not much, then run it, and when it breaks, know you have a pretty big hassle and expense ahead of you.
This is (to me) a craps table gamble... you can keep rolling the point over and over, but eventually you'll roll a 7. How's your luck? And speaking of, you need to factor in 2020. Normally, no, but after this year... while it's apart I'd drop a new Scat into it and not worry, rather than wonder "will THIS be the trip that breaks my baby?" every time you venture forth.
That's just my opinion. Just the crack being there means there's damage in the metal of the crank.... and that means while the linear crack may not fail, nothing will stop that crystalline structure from biting you elsewhere.
This is (to me) a craps table gamble... you can keep rolling the point over and over, but eventually you'll roll a 7. How's your luck? And speaking of, you need to factor in 2020. Normally, no, but after this year... while it's apart I'd drop a new Scat into it and not worry, rather than wonder "will THIS be the trip that breaks my baby?" every time you venture forth.
That's just my opinion. Just the crack being there means there's damage in the metal of the crank.... and that means while the linear crack may not fail, nothing will stop that crystalline structure from biting you elsewhere.
-
- Posts: 366
- Joined: Sun Jan 06, 2019 2:25 pm
- First Name: Dick
- Last Name: Fischer
- * REQUIRED* Type and Year of Model Ts owned: 1912 Touring
- Location: Arroyo Grande, CA
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
James, in your original post you said, "First thing I did is have the crankshaft magnafluxed as always."
Have you actually magnafluxed this particular crank in the past ? Was this same flaw seen previously ? If yes, then the only question you need to consider is whether it has grown since the last time you looked at it. If you have looked at the crank before and this is the first time you have seen the flaw, then I'd be worried.
The other possibility is that this is the first time you have ever inspected the crank and you have no idea if the flaw is a long time feature. Then we're not much smarter other than your observation of the wear evidence along the edges of the flaw.
Making the decision to replace or not is another subject. Is this the original block with correct serial number ? If so, it may have some intrinsic value and you would be more interested in protecting the block. If it's not the original block, then your only decision is whether to definitely spend a good wad of cash now or (maybe) to spend a somewhat larger wad sometime in the future.
Your decision is a lot like buying insurance. What is the chance the event will occur ? What is the cost of the potential occurrence ? How much money are you willing to spend to offset the cost of some potential greater cost in the future ?
Dick
Have you actually magnafluxed this particular crank in the past ? Was this same flaw seen previously ? If yes, then the only question you need to consider is whether it has grown since the last time you looked at it. If you have looked at the crank before and this is the first time you have seen the flaw, then I'd be worried.
The other possibility is that this is the first time you have ever inspected the crank and you have no idea if the flaw is a long time feature. Then we're not much smarter other than your observation of the wear evidence along the edges of the flaw.
Making the decision to replace or not is another subject. Is this the original block with correct serial number ? If so, it may have some intrinsic value and you would be more interested in protecting the block. If it's not the original block, then your only decision is whether to definitely spend a good wad of cash now or (maybe) to spend a somewhat larger wad sometime in the future.
Your decision is a lot like buying insurance. What is the chance the event will occur ? What is the cost of the potential occurrence ? How much money are you willing to spend to offset the cost of some potential greater cost in the future ?
Dick
-
- Posts: 1057
- Joined: Thu Feb 21, 2019 1:20 pm
- First Name: Joe
- Last Name: Bell
- * REQUIRED* Type and Year of Model Ts owned: 24 Fordor
- Location: Tiffin Ohio
- MTFCI Number: 24066
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
I have seen forging lines run across two throws of a crank, they look like cracks on a wet mag machine but they are rolled pieces of steel in the forging, this could be one of those? not saying it is but possible?
-
- Posts: 33
- Joined: Sun Jan 06, 2019 8:53 pm
- First Name: Art
- Last Name: Wilson
- * REQUIRED* Type and Year of Model Ts owned: 1911 Touring
- Location: San Diego
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
Many years ago while on a tour I had number 1 rod get loose in a freshly rebuilt engine. When I dissembled the engine I found a longitudinal crack on number 1 crank journal. It was about 3/4 inch long and could barely be felt by dragging a fingernail across it.
So I'm of the opinion to get a good used crank.
Also check for main bearing wear. The center bearing wears faster than the others, and the looseness is often taken up by removing shims. That puts the crank out of alignment and leads to crank breakage, usually at one of the rod journals.
Art
So I'm of the opinion to get a good used crank.
Also check for main bearing wear. The center bearing wears faster than the others, and the looseness is often taken up by removing shims. That puts the crank out of alignment and leads to crank breakage, usually at one of the rod journals.
Art
-
- Posts: 3002
- Joined: Sun Jan 06, 2019 4:06 pm
- First Name: Jerry
- Last Name: Van
- Location: S.E. Michigan
- MTFCA Number: 24868
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
I say it's a forging flaw and not a crack. "Crack" suggests something that was not always there, but has developed over time, use, stress, etc. I would propose that what you're seeing has been there since day one.
-
- Posts: 405
- Joined: Sun Jan 06, 2019 12:56 pm
- First Name: Rick
- Last Name: Duquette
- * REQUIRED* Type and Year of Model Ts owned: 1913 Touring, 1914 Touring, 1925 Touring, 1927 PU, 1955 T Bird, 69 Shelby GT 350
- Location: Grand Forks, North Dakota
- MTFCA Number: 21848
- MTFCI Number: 22173
- Board Member Since: 2015
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
Find a used/new crank and replace it. The car has been in your family for many years and you will be passing on to a family member. This has been an interesting post with lots of info, but its time to fix your car for the next owner.
-
- Posts: 245
- Joined: Tue Oct 29, 2019 4:14 pm
- First Name: Greg
- Last Name: Popove
- Location: Olds AB
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
I agree. What's to gain by taking a chance on it?
-
- Posts: 663
- Joined: Fri Jan 04, 2019 11:15 am
- First Name: Tony
- Last Name: Bowker
- * REQUIRED* Type and Year of Model Ts owned: 1914 touring
- Location: La Mesa, CA
- MTFCA Number: 32
- MTFCA Life Member: YES
- Board Member Since: 2005
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
I remember speaking to Bruce McCalley on this very subject, well actually was it worth magnafluxing a model T crank. He advised not bothering as most T cranks show some crack somewhere. So on my coupe, which was rebuilt in 1990, was just reground and rebabbitted. So far it’s been fine.
Of course both the speedster and the 14 touring broke cranks while in use and previous writers are correct, it’s expensive.
Has anyone real first hand experience of finding an original Ford crank that has shown no cracks after magnafluxing.
By the way just reboring often doesn’t work as the end play on #3 main bearing us not correct. I tried doing that on the speedster and the end play and crank placement was way off what it should be in a good motor.
Of course both the speedster and the 14 touring broke cranks while in use and previous writers are correct, it’s expensive.
Has anyone real first hand experience of finding an original Ford crank that has shown no cracks after magnafluxing.
By the way just reboring often doesn’t work as the end play on #3 main bearing us not correct. I tried doing that on the speedster and the end play and crank placement was way off what it should be in a good motor.
Tony Bowker
La Mesa, California
1914 Touring, 1915 Speedster, 1924 Coupe.
La Mesa, California
1914 Touring, 1915 Speedster, 1924 Coupe.
-
- Posts: 97
- Joined: Wed Jan 09, 2019 6:46 pm
- First Name: John
- Last Name: Gulbankian
- Location: Massachusetts
- Contact:
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
Quote "Has anyone real first hand experience of finding an original Ford crank that has shown no cracks after magnafluxing. "
Yes we have.
We had a customer a while back go to Langs to see what they had for cranks and Lang's Allowed him to choose the ones he wanted as he only needed one but brought three for us to test. Once they were cleaned all passed the test. It does happen. Not everyone can afford a Scat crank. Though most often the engine we get to rebuild the cranks are usually cracked due to hard driving and being nearly 100 years old.
Yes we have.
We had a customer a while back go to Langs to see what they had for cranks and Lang's Allowed him to choose the ones he wanted as he only needed one but brought three for us to test. Once they were cleaned all passed the test. It does happen. Not everyone can afford a Scat crank. Though most often the engine we get to rebuild the cranks are usually cracked due to hard driving and being nearly 100 years old.
-
- Posts: 1069
- Joined: Sun Jan 06, 2019 12:18 pm
- First Name: John
- Last Name: Warren
- * REQUIRED* Type and Year of Model Ts owned: 14 Roadster, 25 Pickup , 26 Canadian Touring , and a 24-28 TA race car
- Location: Henderson, Nevada
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
We had a crack similar to that on an equipment crankshaft. We ground the crack some just to get rid of the sharp edge running against the bearing , and ran it. It never did brake, but the bearing did go out again. This was done in frame.
24-28 TA race car, 26 Canadian touring, 25 Roadster pickup, 14 Roadster, and 11AB Maxwell runabout
Keep it simple and keep a good junk pile if you want to invent something
Keep it simple and keep a good junk pile if you want to invent something
-
- Posts: 387
- Joined: Sun Jan 06, 2019 7:19 pm
- First Name: Jack
- Last Name: Putnam
- Location: Bluffton, Ohio
- MTFCA Number: 13833
- MTFCI Number: 13353
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
Yes I have, they are out there, but you have to search.
-
- Posts: 1186
- Joined: Mon Jan 07, 2019 10:27 am
- First Name: John
- Last Name: Codman
- * REQUIRED* Type and Year of Model Ts owned: 1927 Youring
- Location: Naples, FL 34120
Re: Dare we analyze my cracked crankshaft?? I say we do.. but INTELLIGENTLY
My biggest concern would be that as Norman Kling said, you would have an obligation to tell any person that you might someday sell the car to that it has a cracked crankshaft. If I were that potential purchaser, in my mind I would be thinking that before I ever drive the car, the engine has to come out and have the crank replaced. If I'm going that far, the engine would have to be disassembled and at least the rings and babbitt inspected carefully. To say that this would have an impact on what I would be willing to pay for the car would be like Noah saying "it looks like a little rain."