OT lathe question
Forum rules
If you need help logging in, or have question about how something works, use the Support forum located here Support Forum
Complete set of Forum Rules Forum Rules
If you need help logging in, or have question about how something works, use the Support forum located here Support Forum
Complete set of Forum Rules Forum Rules
-
Topic author - Posts: 2
- Joined: Tue Jan 08, 2019 4:58 pm
- First Name: Steve
- Last Name: Addington
- Location: St. Maries Idaho
OT lathe question
Hay guys, I have a early 1950 vintage Lablond 13 X 48 lathe. Lathe is in pretty good shape and is tight. The issue I am having is the top spindle speed is only 550 rpm. I am having problems making a really smooth finish when OD turning. I have played with my feed speeds and of course the slower I feed it the better the finish but it is never really nice and smooth like it should be. I am not a life long machinist but am not a newbie either. My tool height is correct, I have tried both high speed steel, sharpened to the correct angles and honed after sharpening and carbide inserts but still am unable to achieve a really smooth finish. I think some of it may be the junk steel that is available now days. I wonder about this because I chucked up an old model A rear axle that I had lying around and turned it down to use for another project and it turned really nice with a nice finish. So after rambling on here my question is, what would be the down side to changing the shiv on the motor and increasing the top speed to around 800 rpm? Any ideas would be welcome. Thanks
-
- Posts: 2345
- Joined: Sun Jan 06, 2019 11:25 am
- First Name: Dave
- Last Name: Hanlon
- * REQUIRED* Type and Year of Model Ts owned: 24 Touring car
- Location: NE Ohio
- MTFCA Number: 50191
- Board Member Since: 2018
Re: OT lathe question
Have you tried slowing the feed down ?
-
- Posts: 201
- Joined: Sun Jan 06, 2019 6:21 pm
- First Name: George
- Last Name: Andreasen
- * REQUIRED* Type and Year of Model Ts owned: 0...building from parts
- Location: Alturas, California
Re: OT lathe question
Don't fiddle with modifying spindle speeds until you find the actual problem.
On any gearbox style lathe, your feed speed (and hence, your finish) determines the result. Since the feed speed is determined by the finest thread setting, spindle speed doesn't affect it much. In fact, most of my ancient machinist books recommend the highest spindle speed and a slow feed speed with a tool sharpened with a whetstone. I would recommend that you visit the "Practical Machinist" website and go to the antique section. Ask for help there, and you'll get some excellent advice from many old timers who know the machines inside and out.
Think you've got problems? I spent the better part of six months rebuilding a Hendey cone head (flat belt) lathe back to truth, only to find out that my finest feed was 80 t.p.i. ! I went through the same routine as you, playing with tool angles, etc. and found the best results were with a healthy round radius on the tool and razor sharp edges. That reduced the "threading" effect of a narrower radius, but it's still not perfect. Suits my needs though. If I need a really "perfect" finish, out comes the tool post grinder with a fine stone!
On any gearbox style lathe, your feed speed (and hence, your finish) determines the result. Since the feed speed is determined by the finest thread setting, spindle speed doesn't affect it much. In fact, most of my ancient machinist books recommend the highest spindle speed and a slow feed speed with a tool sharpened with a whetstone. I would recommend that you visit the "Practical Machinist" website and go to the antique section. Ask for help there, and you'll get some excellent advice from many old timers who know the machines inside and out.
Think you've got problems? I spent the better part of six months rebuilding a Hendey cone head (flat belt) lathe back to truth, only to find out that my finest feed was 80 t.p.i. ! I went through the same routine as you, playing with tool angles, etc. and found the best results were with a healthy round radius on the tool and razor sharp edges. That reduced the "threading" effect of a narrower radius, but it's still not perfect. Suits my needs though. If I need a really "perfect" finish, out comes the tool post grinder with a fine stone!
-
- Posts: 1190
- Joined: Sun Jan 06, 2019 11:08 am
- First Name: DAN
- Last Name: MCEACHERN
- * REQUIRED* Type and Year of Model Ts owned: too many. '14 touring, 2 depot hacks, 2 speedsters
- Location: ALAMEDA,CA,USA
Re: OT lathe question
You will find it difficult to get a good finish on most any steel part with carbide unless you can get the surface speed up around 300-400 feet/min.
Consider changing the size of the motor pulley to increase your top speed. Those old leblonds are great machines just not made for carbide turning on smaller diameters. You don't say what your junk steel is, but you might well be correct if you are turning Chinese water pipe or some such material.
Consider changing the size of the motor pulley to increase your top speed. Those old leblonds are great machines just not made for carbide turning on smaller diameters. You don't say what your junk steel is, but you might well be correct if you are turning Chinese water pipe or some such material.
-
- Posts: 2
- Joined: Sun Jan 06, 2019 10:55 pm
- First Name: Brian
- Last Name: Billing
- * REQUIRED* Type and Year of Model Ts owned: 1923 tourer
- Location: New Zealand
Re: OT lathe question
Using cutting oil will probably help
-
- Posts: 6435
- Joined: Sun Jan 06, 2019 11:18 am
- First Name: Scott
- Last Name: Conger
- * REQUIRED* Type and Year of Model Ts owned: '13, '15, '19, '23
- Location: Clark, WY
- Board Member Since: 2005
Re: OT lathe question
I believe much of your problem is in the steel you're trying to cut. So long as you're not welding it, 12L14 if fabulous stuff to turn; 1018 if you're going to weld it, or case harden it; 1045 if you wish to harden it (but is not too great for lathe work...just thought I throw it in for info). Different steels are for different applications...just picking up a rusty rod off of grandpa's barn floor and expecting it to turn nicely would be like making a canoe out of pecky cypress and expecting a dry trip...some things just are not meant to be.
If you are in a city big enough to have a scrap yard, go there and look for a barrel of nicely turned identical parts that have been scrapped. This will have come from a screw machine shop and the stuff they use is perfect for home shop use...you can be nearly guaranteed that anything of any useful size that is pulled from that barrel will turn exceptionally well.
In the event that you are not able to frequent a scrap yard, a place like this will be your best bet: https://www.onlinemetals.com/merchant.c ... op_cat=197
If you are in a city big enough to have a scrap yard, go there and look for a barrel of nicely turned identical parts that have been scrapped. This will have come from a screw machine shop and the stuff they use is perfect for home shop use...you can be nearly guaranteed that anything of any useful size that is pulled from that barrel will turn exceptionally well.
In the event that you are not able to frequent a scrap yard, a place like this will be your best bet: https://www.onlinemetals.com/merchant.c ... op_cat=197
Scott Conger
Tyranny under the guise of law is still Tyranny
NH Full Flow Float Valves
Obsolete carburetor parts manufactured
Tyranny under the guise of law is still Tyranny
NH Full Flow Float Valves
Obsolete carburetor parts manufactured
-
- Posts: 167
- Joined: Mon Jan 07, 2019 3:48 pm
- First Name: Kim
- Last Name: Wynn
- * REQUIRED* Type and Year of Model Ts owned: 1923 Roadster & 1927 Speedster
- Location: Morris, IL
Re: OT lathe question
Are you using a live or dead center in the tailstock? If not, you may be experiencing vibration of the piece being turned.
I also think like earlier answers and your thought that cheap steel may be "tearing" vs cutting.
In a past life I was a machinist. You might be surprised at what a file and / or Emory cloth would clean up.
I also think like earlier answers and your thought that cheap steel may be "tearing" vs cutting.
In a past life I was a machinist. You might be surprised at what a file and / or Emory cloth would clean up.
-
- Posts: 4967
- Joined: Sat Jan 05, 2019 1:57 pm
- First Name: Mark
- Last Name: Gregush
- * REQUIRED* Type and Year of Model Ts owned: 1925 cutdown PU, 1920 Dodge touring, 1948 F2 Ford flat head 6 pickup 3 speed
- Location: Portland Or
- MTFCA Number: 52564
- Board Member Since: 1999
Re: OT lathe question
You might be surprised at what a file and / or Emory cloth would clean up..I did the bushing area finishing on my shortened drive shaft that way. I have had the worst luck doing anything with drill rod. I wish I could remember which I used, but it might have been the 1018, nice to work with.
I know the voices aren't real but damn they have some good ideas!
1925 Cut down pickup
1920 Dodge touring
1948 Ford F2 pickup
1925 Cut down pickup
1920 Dodge touring
1948 Ford F2 pickup
-
- Posts: 10
- Joined: Mon Jan 07, 2019 8:13 am
- First Name: Don
- Last Name: Keil
- * REQUIRED* Type and Year of Model Ts owned: 26 roadster
- Location: Montana
Re: OT lathe question
not familiar with the lablond but a buddy could not slow his lathe down. he did not know his lathe had a back gear.
-
- Posts: 60
- Joined: Tue Jan 08, 2019 7:35 pm
- First Name: David
- Last Name: Sullivan
- * REQUIRED* Type and Year of Model Ts owned: 1923
- Location: Bellingham WA
Re: OT lathe question
My experience is, you can't hardly machine A36 steel smooth, made in China, or not. By far the most common steel "lying around". Dave in Bellingham,WA
-
- Posts: 278
- Joined: Sun Jan 06, 2019 3:08 pm
- First Name: Bob
- Last Name: Doris
- * REQUIRED* Type and Year of Model Ts owned: 1926 Runabout, 1930 Sport Coupe
- Location: Prescott, Arizona
- MTFCA Number: 32538
- Board Member Since: 2017
Re: OT lathe question
Cold rolled steel (e.g.1018) tends to tear when turning. Surface finish can be improved as others have stated by application of emery cloth or tool post grinding.
Steels I have found that turn nicely include 4000 series alloy, 12L14 and A2 tool steel.
550 Rpm max spindle speed is quite slow. Good for turning large diameters. I don’t see any reason not to try increasing the spindle speed to 800 rpm for smaller diameter turning.
Steels I have found that turn nicely include 4000 series alloy, 12L14 and A2 tool steel.
550 Rpm max spindle speed is quite slow. Good for turning large diameters. I don’t see any reason not to try increasing the spindle speed to 800 rpm for smaller diameter turning.
-
- Posts: 2998
- Joined: Sun Jan 06, 2019 4:06 pm
- First Name: Jerry
- Last Name: Van
- Location: S.E. Michigan
- MTFCA Number: 24868
Re: OT lathe question
Does your cutting tool have any kind of tip radius, or are you sharpening it to a point? Try using a .015 - .030 tip radius, along with a little bit of cutting oil. Also, check the ways on your compound to check for any slop. The gibs should be adjusted for just a slight drag.
-
- Posts: 10
- Joined: Tue Jan 15, 2019 10:59 am
- First Name: Keith
- Last Name: Taylor
- Location: Jefferson, Maine
- MTFCA Number: 10631
Re: OT lathe question
I find that I can get an improved finish if I take a second pass without touching the settings. Basically you are cutting a fine thread. If you take a second final pass you will knock off the tops off of the “threads.”
And the posts that recommend 12L14 (Ledloy) are right on the money.
Keith
And the posts that recommend 12L14 (Ledloy) are right on the money.
Keith